Cordierite DPF Diesel Particulate Filter for auto exhaust
With increasing appearance of diesel engine automobile, the particulate from emission, mainly carbon, enhances the pollution to the environment. Regulation for diesel engine, stipulating the particulate in diesel passenger cars emission should meet the criterion: below 2.0g/mile. The diesel particulate filter is able to filter above 80% carbon smoke particulate. For practical application, it would be a great help to solve the problem of air pollution.
If the DPF is coated with precious-metal (such as Pt, Pd and Rh), black smoke with carbon particulate from diesel engine pass through a special tube and enter the filter. The carbon smoke particulate is absorbed to the filter made of metallic fiber felt, when passing the inner dense set and bag-style filter. When particulate absorption reaches some degree, the tail burner would be ignited to burn automatically. In this case, the particulate absorbed been burned out and turned into nontoxic CO2 then discharge. The full device is designed as double room structure, and filtration and recycle are going in different areas, making them non-disturbed. The system can work automatically whatever working condition the engine in. especially made honeycomb ceramic particulate filter, acts as capturing device to the particulate to some extent.
The particulate of emission is captured inside thin gas hole or entrance. As it lasts, the cumulated layer become thick, and pressure loss increase. To ensure the performance of engine, when pressure loss reaches some value, it is a must to recycle the filter. The recycle is making the particulate burning, by raising the gas temperature of filter.
The particulate condition is related to the oxygen concentration. Normally, it is burning at 550-650 .Its adopted to raise emission temperature by adjusting throttle, and increase gas temperature with burner. The particulate burning temperature can be decreased by catalyzed, making cumulative particulate burning as soon as possible, thus recover the pressure loss and fitters performance, then the filter is recycled.
Physical Properties
Applicable size range: D (5.66"-12") * L (5"-12")
|
Items |
Specifications |
||
|
100 cpsi |
200 cpsi |
300 cpsi |
|
|
Diameter |
±1.5 mm |
±1.5 mm |
±1.5 mm |
|
Length |
±2.0 mm |
±2.0 mm |
±2.0 mm |
|
Verticality |
≤2 mm |
≤2 mm |
≤2 mm |
|
Parallelism |
≤2 mm |
≤2 mm |
≤2 mm |
|
Pore density |
100±15 cpsi |
200±20 cpsi |
300±20 cpsi |
|
Wall thickness |
0.55±0.06 mm |
0.35±0.03 mm |
0.3±0.03 mm |
|
Plugging depth |
5±1 mm |
5±1 mm |
5±1 mm |
|
|
Properties |
Note |
||
|
100 cpsi |
200 cpsi |
300 cpsi |
||
|
Compressive Strength |
A axis direction≥12MPa; B axis direction≥2Mpa |
|
||
|
Water absorption |
22%~28% |
|
||
|
Porosity |
44%±3% |
|
||
|
Coefficient of thermal expansion |
≤4.3×10-6/℃ |
Room temperature -800℃ |
||
|
Softening Temperature |
≥1900 ℃ |
|
||
|
Thermal shock resistence |
≥3 Cycles without split @400℃ |
|
||
|
Initial back pressure |
＜0.4 (10.5*7) kPa |
＜4.5 (5.66*6) kPa |
<5.8 (5.66*6) kPa |
@room temperature, 600Nm3/h |
|
Heat conductivity |
43 (298) W/m.K |
|
||
|
Isostatic pressure |
≥1.05 MPa |
|
||
|
Average aperture |
19 μm |
18 μm |
18 μm |
|
|
SiC crystal content |
>99% |
|
||
1. Recrystallized silicon carbide.
2. Diameter from 5.66'' to 13'', normally5.66'', 7.5'', 8.75'', 10.5'', 11.25'', 12''.
3. Length from 5'' to 13'', normally6'', 7'', 7.5'', 8'', 10'', 12''.
4. 100cpsi, 200cpsi, symmetric 300cpsi and asymmetric 300cpsi are availiable.
5. Other sizes could be produced according to your requirements.
6. Could be marked and packaged according to your requirements.
Hot Tags: cordierite dpf honeycomb ceramic, China cordierite dpf honeycomb ceramic manufacturers, factory, Honeycomb Ceramic Plate for Casting, Cordierite DPF Honeycomb Ceramic, SCR Honeycomb Ceramic, Infrared Honeycomb Ceramic Plate for BBQ, Honeycomb Ceramic, RTO Heat Exchange Honeycomb Ceramic